316LN is a low carbon stainless steel

316LN is a low carbon stainless steel with excellent corrosion and heat resistance for a wide range of applications.

Chemical composition:

Carbon C: ≤0.08

Manganese Mn: ≤2.00

P: ≤0.045

Sulfur S: ≤0.030

Si: ≤1.0

Cr: 16.0 to 18.0

Nickel Ni: 10.0-13.0

Molybdenum Mo: 2.0-3.0

Nitrogen N: 0.10-0.16

Mechanical properties:

Tensile strength: ≥550MPa

Yield strength: ≥205MPa

Elongation: ≥40%

Hardness: ≤217HB

Corrosion resistance:

Having good humus in general humus, such as acid, base, salt, etc.

Excellent resistance to heat and decay at high temperatures.

It has good antioxidant capacity and is suitable for some special fields.

Application field:

Chemical, petroleum and natural gas industries: 316LN stainless steel material is widely used in the chemical, petroleum and natural gas industries in high temperature and high pressure environment equipment and pipe.

Nuclear Energy Industry: 316LN stainless steel is also suitable for piping and equipment in nuclear reactors due to its excellent corrosion resistance to high temperature, high temperature illuminator environments.

Medical equipment: 316LN stainless steel can also be used in the manufacture of medical equipment, such as hand instruments, human-made joints, etc.

Precautions for use:

In the process of processing and welding, good processing temperature should be controlled to avoid the influence of too high temperature on the steel material that is not sharp.

In the process of use, should avoid long time contact with high temperature partial ion concentration environment, so as to avoid the steel material manufacturing rot and damage.